ASTM A231
2020-04-09 18:33:44
|
|
|
Specification and Steel Grade |
: |
ASTM A231 |
Type |
: |
Alloy Steel |
|
|
|
Main Chemical Compositions|(%) |
: |
C0.48~0.53,Cr0.80~1.10,V≥0.15 |
|
|
|
Strength of Extension|σb/MPa |
: |
1310~2070 |
Elasticity Modulus|E/GPa |
: |
210 |
Torsional Property|σb Min(%) |
: |
45 |
Rigidity Modulus|G/GPa |
: |
80 |
Hardness|HRC |
: |
41~55 |
Working Temperature|/℃ |
: |
220 |
Features and Use |
: |
CrV steel for spring by impact load and high temperature work.ASTMA232 used as valve spring |
|
|
|
Remark: |
|
|
①, For helical compression spring or tension spring, the distorting stress should be 75% of σb minimum. |
②, It is the United States federal specification. |
|
|
|
|
|
|
ASTM A231
2020-04-09 18:33:44
|
|
|
Specification and Steel Grade |
: |
ASTM A231 |
Type |
: |
Alloy Steel |
|
|
|
Main Chemical Compositions|(%) |
: |
C0.48~0.53,Cr0.80~1.10,V≥0.15 |
|
|
|
Strength of Extension|σb/MPa |
: |
1310~2070 |
Elasticity Modulus|E/GPa |
: |
210 |
Torsional Property|σb Min(%) |
: |
45 |
Rigidity Modulus|G/GPa |
: |
80 |
Hardness|HRC |
: |
41~55 |
Working Temperature|/℃ |
: |
220 |
Features and Use |
: |
CrV steel for spring by impact load and high temperature work.ASTMA232 used as valve spring |
|
|
|
Remark: |
|
|
①, For helical compression spring or tension spring, the distorting stress should be 75% of σb minimum. |
②, It is the United States federal specification. |
|
|
|
|
|
|