ASTM A229
2020-04-08 09:14:22
|
|
|
|
|
Specification and Steel Grade |
: |
ASTM A229 |
|
Type |
: |
High-Carbon Steel |
|
|
|
|
|
Main Chemical Compositions|(%) |
: |
C0.55～0.85，Mn0.30～1.20 |
|
|
|
|
|
Strength of Extension|σb/MPa |
: |
I grade:1140～2020，II grade:1320～2330 |
|
Elasticity Modulus|E/GPa |
: |
210 |
|
Torsional Property|σb Min(%) |
: |
45 |
|
Rigidity Modulus|G/GPa |
: |
80 |
|
Hardness|HRC |
: |
42～55 |
|
Working Temperature|/℃ |
: |
120 |
|
Features and Use |
: |
Used for general purposes of spring,need heat treatment before produce |
|
|
|
|
|
Remark: |
|
|
|
①, For helical compression spring or tension spring, the distorting stress should be 75% of σb minimum. |
|
②, It is the United States federal specification. |
|
|
|
|
|
|
|
|
ASTM A229
2020-04-08 09:14:22
|
|
|
|
|
Specification and Steel Grade |
: |
ASTM A229 |
|
Type |
: |
High-Carbon Steel |
|
|
|
|
|
Main Chemical Compositions|(%) |
: |
C0.55～0.85，Mn0.30～1.20 |
|
|
|
|
|
Strength of Extension|σb/MPa |
: |
I grade:1140～2020，II grade:1320～2330 |
|
Elasticity Modulus|E/GPa |
: |
210 |
|
Torsional Property|σb Min(%) |
: |
45 |
|
Rigidity Modulus|G/GPa |
: |
80 |
|
Hardness|HRC |
: |
42～55 |
|
Working Temperature|/℃ |
: |
120 |
|
Features and Use |
: |
Used for general purposes of spring,need heat treatment before produce |
|
|
|
|
|
Remark: |
|
|
|
①, For helical compression spring or tension spring, the distorting stress should be 75% of σb minimum. |
|
②, It is the United States federal specification. |
|
|
|
|
|
|
|
|